A surface crack in a graded coating bonded to a homogeneous substrate under general loading conditions

Sami El-Borgi*, Radhi Abdelmoula, Serkan Dag, Nizar Lajnef

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

4 Citations (Scopus)

Abstract

The elastostatic problem of a surface crack in a graded coating bonded to a homogeneous substrate under general loading conditions is considered. The coating is graded along the thickness direction and modeled as a nonhomogeneous medium with an isotropic stress-strain law. The problem is solved under the assumption of plane strain or generalized plane stress conditions. The crack surfaces are subjected to arbitrary loadings which give rise to mixed fracture modes which can be uncoupled due to the fact that the crack axis is parallel to the material gradient. Therefore, the opening and sliding mode problems may be formulated separately. For each problem, the solution of the composite medium may be determined by obtaining the solution of the homogeneous substrate and that of the graded layer. The latter solution may be expressed as the sum of two solutions, namely an infinite graded medium with a crack and a graded strip without a crack. The resulting mixed-boundary value problem is reduced to a set of two uncoupled singular integral equations which are solved numerically using Jacobi polynomials. The main objective of the paper is to study the effect of the layer thickness and nonhomogeneity parameter on the crack tip mixed-mode stress intensity factors for the purpose of gaining better understanding on the behavior of graded coatings.

Original languageEnglish
Pages (from-to)1331-1353
Number of pages23
JournalJournal of Mechanics of Materials and Structures
Volume2
Issue number7
DOIs
Publication statusPublished - Sept 2007
Externally publishedYes

Keywords

  • Graded coating
  • Mixed-mode loading
  • Singular integral equations
  • Stress intensity factor
  • Surface crack

Fingerprint

Dive into the research topics of 'A surface crack in a graded coating bonded to a homogeneous substrate under general loading conditions'. Together they form a unique fingerprint.

Cite this