Effect of Prestrain on Hydrogen-Induced Delayed Cracking for Medium Mn Steels

Q. Y. Liu, Y. Yan*, J. P. Xu, S. Q. Yang, J. X. Li, Y. J. Su, L. J. Qiao

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

7 Citations (Scopus)

Abstract

Medium Mn steels are a class of the new-generation ultra-high-strength materials used in automotives. However, despite excellent ductility, they may suffer from delayed cracking and thus cause serious concerns. In this study, several medium Mn steels were tested with different prestrain and hydrogen charging conditions. The interaction and synergistic effects of prestrain and hydrogen content on hydrogen-induced delayed cracking behavior are investigated. The threshold stress of hydrogen-induced cracking (HIC) decreased during dynamic hydrogen charging under a constant load. In the process of dynamic hydrogen charging, for M7B and M10B steels, the normalized stress intensity factor σ/σb and the corresponding threshold stress σHIC decreased sharply as prestrain increased. This is because the volume fraction of retained austenite decreased with an increase in prestrain. Similarly, σHIC was reduced and the critical hydrogen content dropped drastically with increasing prestrain. For M7C, the influence of prestrain on threshold stress and hydrogen concentration was less than that of M7B. This is because the different treatment processes leads to a different stability of the retained austenite. By observing the SEM fractographs, the fracture surface of medium Mn steels showed different fracture characteristics, such as dimple fractures and intergranular and transgranular modes.

Original languageEnglish
Pages (from-to)1929-1938
Number of pages10
JournalJournal of Materials Engineering and Performance
Volume29
Issue number3
DOIs
Publication statusPublished - 1 Mar 2020
Externally publishedYes

Keywords

  • delayed cracking
  • hydrogen embrittlement
  • medium Mn steel