In situ micromechanical testing in environmental scanning electron microscope: A new insight into hydrogen-assisted cracking

Bjørn Rune Sørås Rogne*, Nousha Kheradmand, Yun Deng, Afrooz Barnoush

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

33 Citations (Scopus)

Abstract

The susceptibility of Fe–26Al–0.5Cr (at.%) intermetallic alloy to hydrogen assisted cracking was evaluated by micromechanical fracture mechanics specimens. The notched micro-beams were loaded in situ in an environmental scanning electron microscope under two conditions: one with low pressure to avoid any hydrogen effect and the other with water vapour to promote hydrogen uptake and hydrogen assisted cracking. Fractographic and electron backscatter diffraction analysis carried out on the fracture surfaces of the ruptured beams revealed the mechanisms of the crack propagation. Under both conditions, the failure was cleavage-like, accommodated with plastic deformation. The results show the influence of hydrogen-induced embrittlement on the initiation of the fracture and the plasticity of the crack tip during the propagation of the crack, where the latter becomes localised and uniform over the fracture surface. From the observations, a three stage crack propagation process is proposed. Also, the fracture toughness of the samples was evaluated by linear elastic fracture mechanics and the validity of the results are discussed.

Original languageEnglish
Pages (from-to)257-268
Number of pages12
JournalActa Materialia
Volume144
DOIs
Publication statusPublished - 1 Feb 2018
Externally publishedYes

Keywords

  • Environment-assisted cracking
  • Fracture mechanisms
  • Hydrogen embrittlement
  • Intermetallics (iron-aluminides)
  • Micromechanics

Fingerprint

Dive into the research topics of 'In situ micromechanical testing in environmental scanning electron microscope: A new insight into hydrogen-assisted cracking'. Together they form a unique fingerprint.

Cite this